Refractory Brick Material In Clay Brick Plant Red Clay Brick Production Line Fired Bricks
Products description of Refractory Bricks in Clay Brick Plant Red Clay Brick Production Line Fired Bricks
Low thermal conductivity anti-stripping brick is characterized by: synthesizing low thermal conductivity and alkali-resistant raw materials, using alumina fine powder, andalusite and bound clay as raw materials, mixing to make mixed powder, and then adding the mixed powder into a binder, pressing After forming, drying and firing, the bricks with low thermal conductivity and spalling resistance are obtained.
Application of refractory bricks in red clay brick production line of clay brick factory Fired bricks: tunnel kiln; cement kiln: safe area, rotary kiln preheating/calcining area.
Features of refractory bricks for clay brick factory Red clay brick production line Fired bricks: Excellent resistance to alkali erosion Excellent thermal shock resistance Low thermal conductivity Reduced kiln shell load, lining mechanical stress
Parameters of Refractory Bricks in Clay Brick Plant Red Clay Brick Production Line Fired Bricks : Outstanding resistance to alkali attack Excellent thermal-shock resistance Low thermal conductivity Decreasing the kiln shell load, the mechanical stress on the lining
| CHEMICAL COMPOSITION | SPEC | TYPICAL |
| Al2O3 | | % | ≤35 | 32-34 |
| SiO2 | | % | | 62-64 |
| Fe2O3 | | % | ≤1.8 | 1.6 |
| PHYSICAL PROPERTIES | | | SPEC | TYPICAL |
| Thermal Shock Resistance | TSR - in water at 1100 °C | cycle | ≥15 | 16 |
| Refractoriness Under Load | RUL (0.2MPa) | °C | ≥1310 | 1330 |
| Thermal Expansion | TE- 1000 °C | % | | 0.6 |
| Cold Crushing Strength | CCS | MPa | ≥45 | 57 |
| Thermal Conductivity | TC - 700士25 °C | W/m.K | ≤1.5 | 1.5 |
| Alkali Resistance | 1100 °C*5h | | First grade |
Applications of Refractory Bricks in Clay Brick Plant Red Clay Brick Production Line Fired Bricks in Brick Making Plant.