Refractory Brick Material Fired Bricks In Clay Brick Plant And Auto Ceramics Plant
Products description of Refractory Materials Fired Bricks in Clay Brick Plant and Auto Ceramics Plant
Low thermal conductivity and anti-stripping brick, which is characterized by: synthetic low-conductivity and thermal-alkali-resistant raw materials, alumina fine powder, andalusite And bound clay as raw materials, mixed to make a mixed powder, and then added a binding agent to the mixed powder, pressed into shape, dried, and fired to obtain the low thermal conductivity anti-stripping brick.
Application of Refractory Materials Fired Bricks in Clay Brick Plant and Auto Ceramics Plant:Tunnel kiln;Cement Kilns :Safety zone, Pre-heating /Calcining zone in rotary kiln.
Features of Refractory Materials Fired Bricks in Clay Brick Plant and Auto Ceramics Plant : Outstanding resistance to alkali attack Excellent thermal-shock resistance Low thermal conductivity Decreasing the kiln shell load, the mechanical stress on the lining
Parameters of Refractory Materials Fired Bricks in Clay Brick Plant and Auto Ceramics Plant: Outstanding resistance to alkali attack Excellent thermal-shock resistance Low thermal conductivity Decreasing the kiln shell load, the mechanical stress on the lining
| CHEMICAL COMPOSITION | SPEC | TYPICAL |
| Al2O3 | | % | ≤35 | 32-34 |
| SiO2 | | % | | 62-64 |
| Fe2O3 | | % | ≤1.8 | 1.6 |
| PHYSICAL PROPERTIES | | | SPEC | TYPICAL |
| Thermal Shock Resistance | TSR - in water at 1100 °C | cycle | ≥15 | 16 |
| Refractoriness Under Load | RUL (0.2MPa) | °C | ≥1310 | 1330 |
| Thermal Expansion | TE- 1000 °C | % | | 0.6 |
| Cold Crushing Strength | CCS | MPa | ≥45 | 57 |
| Thermal Conductivity | TC - 700士25 °C | W/m.K | ≤1.5 | 1.5 |
| Alkali Resistance | 1100 °C*5h | | First grade |
Applications of Refractory Bricks in Clay Brick Plant Red Clay Brick Production Line Fired Bricks in Brick Making Plant.